Shanghai Bozhong Metal Group Co. Ltd

Model Number: ZXL061 Brand Name: Baosteel, TISCO Key Specifications/Special Features: Descriptions:Low alloyed cold work tool steelApplications:Dies, impact resistant toolsChemical composition: (in weight %)C 0.85
Si 0.25
Mn 0.33
Cr 0.20
Ni 0.80
V 0.13
Physical properties (average values) at ambient temperature:
Modulus of elasticity: 210 [10³xN/mm²]
Density: 7.80g/cm³
Soft annealing:
Heat to 700-740°C, cool slowly in furnace, this will produce a maximum Brinell hardness of 220
Stress relieving:
Stress relieving to remove machining stresses should be carried out by heating to approx, 650°C, holding for 1-2 hours at heat, followed by air cooling, this operation is performed to reduce distortion during heat treatment
Hardening:
Harden from a temperature of 770-800°C (for diameter up to 50mm), 800-850°C(for diameter up to 50-80mm) followed by water quenching
Hardness after quenching is 64-66 HRC
Tempering:
Tempering temperature: 150-250°C
Hardness after tempering is 57-63 HRC
Forging:
Hot forming temperature: 1050-850°C

Specifications:
Grade: mat number 1.2770
Standards: DIN, GB
Length: 1500-6000mm
Width: 100-1250mm
Thickness: 0.3-200mm
Certification: ISO
Technical treatment: cold-rolled and hot rolled

Packing and delivery:
Packing: standard export seaworthy packing or as customer's requirements
Delivery: 7-20 days after received deposit of T/T